论文冻融循环作用下表层嵌贴CFRP—混凝土界面黏结性能试验是关于对写作黏结论文范文与课题研究的大学硕士、相关本科毕业论文粘接还是黏结论文开题报告范文和相关文献综述及职称论文参考文献资料下载有帮助。
摘 要：以嵌贴CFRP-混凝土黏结的冻融耐久性为研究对象,通过拔出试验考察了冻融循环作用下嵌贴FRP和具有不同强度或抗冻性能混凝土的黏结性能,讨论了冻融循环下嵌贴FRP-混凝土界面黏结的退化机理；分析了冻融循环作用下混凝土槽至试件边缘距离、胶层厚度等因素对试件界面黏结性能的影响.试验结果表明：冻融循环作用下普通C30混凝土力学性能退化显著,添加引气防冻剂和减水剂的C30混凝土强度下降显著小于普通C30混凝土,C60混凝土强度反而有所提高；冻融循环导致了嵌贴CFRP-普通C30混凝土的黏结承载力下降和破坏模式转变,但嵌贴CFRP和抗冻混凝土间的黏结承载力没有显著降低,表明混凝土冻融损伤是冻融循环下嵌贴FRP-混凝土黏结退化的主要原因；槽壁厚度较小时,加载端槽壁混凝土出现锥形斜裂缝；胶层厚度较薄时,冻融循环作用下试件黏结承载力的降低较胶层较厚的试件更为显著.
关键词：表层嵌贴；CFRP；黏结性能；冻融循环；混凝土
中图分类号：TU378 文献标志码：A
文章编号：1674-2974（2017）05-0063-10
Abstract：The durability of the interface between N FRP and concrete under freeze-thawing cycles was examined. The pull-out tests were conducted to investigate the influence of freeze-thawing cycles on the bond performance between N FRP and concrete with normal strength, high strength, or additional frost resistance. The mechanism of the bond degradation between N FRP and concrete under the freeze-thawing cycles was also discussed. Moreover, the influences of the distance between concrete edge and groove （edge distance） and the thickness of epoxy adhesive on the bond durability of the N FRP were studied. The test results show that freeze-thawing cycling resulted in the strength deterioration of ordinary concrete, while the high strength concrete and the concrete with frost resistance showed no significant deterioration under freeze-thawing cycles. Freeze-thawing cycling also caused the transformation of failure mode and the relatively significant decrease in bond capacity for specimens using ordinary concrete. Nevertheless, it had no substantial impact on the bond performance of specimens made by concrete with high strength or frost resistance. This result indicates that the bond deterioration of N FRP under freeze-thawing cycles was caused by low strength of concrete. Moreover, the decrease of edge distance resulted in cone-shape cracks at the loading end. When the thickness of epoxy adhesive was reduced, the bond strength degradation induced by freeze-thawing cycles was more significant compared with that of specimens with thicker epoxy adhesive.
Key words：near-surface mounted； CFRP； bond performance； freeze-thawing cycles； concrete
纖维增强复合材料（Fiber Reinforced Polymer,FRP）具有轻质、高强和耐久性好等优点,被广泛应用于土木工程结构的加固[1].但目前应用的外贴（Externally bonded,EB） FRP方法加固混凝土结构尤其是受弯构件时,容易发生FRP和结构之间的剥离,导致加固效率降低和结构过早失效.近年来表层嵌贴（Near Surface Mounted,N ） FRP技术逐渐得到发展,该技术将FRP 嵌入预先开出的混凝土槽中,通过FRP和混凝土的三面甚至四面黏结,大幅增大两者间的黏结面积,显著提高FRP-混凝土界面的黏结承载力,因此可更好地发挥FRP材料强度,并且FRP材料因嵌入混凝土保护层而拥有了更好的耐久性能,因此表层嵌贴FRP技术在未来的钢筋混凝土结构加固领域具有显著的潜力[2].
总结:本文是一篇关于黏结论文范文，可作为相关选题参考,和写作参考文献。
参考文献：
1、 论武术产业集群在市场循环经济中的作用 摘 要：武术产业是中国体育产业中的一个重要组成部分，武术产业在产业化的实践操作方面及经济体制结构、管理安排方面都體现出极强的活力，并有着光明的发。
2、 PDCA循环护理模式对糖尿病患者低血糖反应预防作用 [摘要] 目的 探讨PDCA循环护理模式的应用对于糖尿病患者低血糖反应的预防效果。方法 选取该院2017年1—7月期间收治的248例糖尿病患者作。
3、 发挥税收职能作用促进柴达木循环经济试验区 自2005年国家批准柴达木循环经济试验区为全国首批13个循环经济示范产业园以来，海西全面确立了“突出资源特色、强化技术创新、培育优势产业、实现循。
4、 阳极跟进作用下软黏土电渗固结室内试验 摘要：在等电势梯度的前提下，针对电渗法加固软黏土地基提出了阳极跟进技术，设计了8组电渗对比试验，对不同阳极跟进方案作用下电渗试验的电流、抗剪强度。
5、 表层嵌贴预应力CFRP板条加固钢筋混凝土梁应力传递行为 摘要：表層嵌贴预应力FRP板条加固钢筋混凝土结构技术可充分发挥FRP材料强度，且不需设置永久锚具，具有较大的潜力。以试验得到的嵌贴FRP混凝土粘。
6、 国家重大政策执行审计作用和组织方式 一、国家重大政策执行审计的作用（一）提高国家重大政策的执行力国家重大政策效果的充分发挥，以政策的充分有效执行为前提。国家重大政策执行审计的核。